Technical specification |
Rare metal catalyst |
Precious metal catalyst -200 |
Precious Metal catalyst -300 |
|
Active Components |
Sc, La, Ce, Pr, etc |
Pt, Pd, Au and other precious metals |
Pt, Pd, Au and other precious metals |
|
Service life |
1-3 years |
1-3 years |
1-3 years |
|
Strengths |
Multi-metal composite, certain resistance to sulfur and chlorine, low cost, widely used |
Precious metal components, high efficiency, low conversion temperature, low operating costs |
Precious metal components, high efficiency, low conversion temperature, low operating costs |
|
appearance |
Square honeycomb, dark black |
Square honeycomb, light yellow |
Square Honeycomb, pale yellow |
|
Carrier |
|
Honeycomb ceramics |
Honeycomb ceramics |
|
Pass and density |
Square hole, 200 CPSI |
Square hole, 200 CPSI |
Square hole, 200 CPSI |
|
Length, width and height |
100 x 100 x 50 (mm) |
100* 100*50 (mm) |
100* 100*50 (mm) |
|
Wall thickness |
0.5mm |
0.5mm |
0.5mm |
|
Outer wall thickness |
1.5mm |
1.5mm |
1.5mm |
|
Single piece quality |
290±10 g |
280±10 g |
280±10 g |
|
Single block volume |
0.5L |
0.5L |
0.5L |
|
Packing density |
560-600 kg/m3 |
540-580 kg/m3 |
540-580 kg/m3 |
|
Catalytic efficiency |
> 96% |
> 97% |
> 98% |
|
Operating temperature |
250-400 ° C |
250-400 ° C |
250-400 ° C |
|
Conversion temperature |
330-350 ° C |
260-300 ℃ |
260-300 ℃ |
|
Instantaneous impactresistance to high temperatures |
700 ° C |
700 ° C |
700 ° C |
|
Airspeed |
8000h- 1- 10000h- 1 |
8000h- 1- 12000h- 1 |
10000h- 1- 15000h- 1 |
|
Specific Heat Capacity |
850- 1000 J/Kg ·K |
850- 1000 J/Kg ·K |
850- 1000 J/Kg ·K |
|
Compressive strength |
A-axis > 18MPa Axis B > 4MPa |
Axis A > 18MPa B axis > 4MPa |
Axis A > 18MPa Axis B > 4MPa |